Water-based, ultra-reflective, self-cleaning and photocatalytic resin-based protective coating.
Yield
– 1.00 kg/m² = 0.204 lb/ft²
Packaging
– 5 kg (11.02 lb) plastic bucket.
– 20 kg (44.09 lb) plastic bucket
– 20 kg (44.09 lb) plastic bucket
Drying time
– 5h
Value referred to +23°C/+73°F and 50% relative humidity
Value referred to +23°C/+73°F and 50% relative humidity
Application
– Brush
– Roll
– Airless
– Roll
– Airless
Characteristics
“Self-cleaning” and photocatalytic liquid coating, formulated with water-based synthetic resins and special additives. The product is able to trigger a photo catalytic process that breaks down pollutants and reduces pollution.
Ecoreflex also guarantees the reflection of sunlight, decreases the temperature of the substrate on which it is applied and therefore reduces the use of air conditioning systems. Ready to use and suitable for covering horizontal and vertical surfaces, sloped walls, as it has good adhesion even on bituminous or slated substrates.
Appearance: Liquid
Components: One-component
Isopropanol conversion (smog simulant) with Vitalus-Osram broad spectrum lamps (300 W): 80% after 24 hours of irradiation.
Smoke test (yellowing 15 days + 3 hours with UVB rays): noticeable whitening (self-cleaning).
Reflection: 82%
Thermal emission (E): 90%
Solar Reflex Index (SRI): 103%
Weathering test: 1680 hours (> 10 years)
Resistance to 50 freeze-thaw cycles (-15°C/+15°C): unchanged
Bending strength: 12 mm // 0.47 in – good.
Break Elongation: 327%
Adhesion on slightly worn bituminous membrane: > 7.0 MPa
Adhesion on slated sheath: 4.3 MPa
Adhesion on galvanized sheet: 1.7 MPa
Adhesion on slate: 2.5 MPa
Adhesion on polyurethane (PU) panel: 1.5 MPa
Elongation at break after 1680 hours of accelerated aging: 166%
Tensile strength after 1680 hours of accelerated aging: 1.12 N/mm2 // 162.44 lb/in2 (psi)
Viscosity (Brookfield DV-E s04 viscometer, 6 rpm: T = 20 ° C, 75% R.H.): 24000 mPa∙s
Highly resistant ultra-reflective coatings
for energy savings
- Self-cleaning
- Excellent smog abatement capabilities.
- It contributes to the reduction of energy requirements for summer air conditioning.
- Reduces the phenomenon of urban heat islands (Heat Island Effect).
- It can be applied to complete waterproofing systems based on synthetic resins.
- High reflection capacity of the sun’s rays.
- High elasticity both at high and low temperatures.
- High re-waterproofing capabilities.
- Easy and quick to apply.
- Solvent free product.